AC system | AC | AC | AC | AC | AC | AC | AC | AC | AC | AC | AC | AC | AC | AC | AC | AC |
type | D42H22 | D42H29 | D42H36 | D42H19.5 | D42H32 | D42H26.4 | D42H29.4 | D46H35.4 | D48H35.4 | D50H24 | D50H36 | D60H35.4 | D64H35.4 | D71H35.4 | D78H35.4 | D99H21.4 |
suggested rated voltage (kV) | 3.3 | 4.4 | 5.4 | 3 | 5 | 4.5 | 5 | 5.5 | 5.5 | 3.7 | 5.6 | 5.6 | 5.6 | 5.7 | 5.7 | 3.5 |
MCOV (kV) | 2.8 | 3.7 | 4.6 | 2.6 | 4.2 | 3.8 | 4.2 | 4.7 | 4.7 | 3.2 | 4.7 | 4.7 | 4.7 | 4.8 | 4.8 | 2.9 |
diameter (mm) | 42±0.7 | 42±0.7 | 42±0.7 | 42±0.7 | 42±0.7 | 42±0.7 | 42±0.7 | 46±1 | 48±1 | 50±2 | 50±3 | 60±1 | 64.5±1 | 70.5±1 | 78±1 | 99±1.2 |
height (mm) | 22±0.3 | 29±0.3 | 36±0.3 | 19.5±0.3 | 32±0.3 | 26.4±0.3 | 29.4±0.3 | 35.4±0.3 | 35.4±0.3 | 24±0.3 | 36±0.3 | 35.4±0.3 | 35.4±0.3 | 35.4±0.3 | 35.4±0.3 | 21.4±0.3 |
DC U1mA (kV) | 4.85±0.3 | 6.4±0.45 | 7.95±0.5 | 4.45±0.3 | 7.3±0.45 | 6.6±0.45 | 7.35±0.45 | 7.8±0.5 | 7.8±0.5 | 5.3±0.3 | 7.9±0.5 | 7.8±0.5 | 7.8±0.5 | 7.8±0.5 | 7.8±0.5 | 4.7±0.35 |
IL at 75% of U1mA (µA) | ≤ 15 | ≤ 15 | ≤ 15 | ≤ 15 | ≤ 15 | ≤ 15 | ≤ 15 | ≤ 20 | ≤ 20 | ≤ 20 | ≤ 20 | ≤ 20 | ≤ 20 | ≤ 20 | ≤ 20 | ≤ 20 |
Ures (kV) | 8.6±0.5 | 11.3±0.7 | 14.1±0.8 | 7.8±0.5 | 12.75±0.8 | 11.45±0.8 | 12.75±0.8 | 13.45±0.8 | 13.45±0.8 | 9.0±0.5 | 13.45±0.8 | 12.95±0.8 | 12.75±0.8 | 12.65±0.8 | 12.45±0.8 | 7.85±0.5 |
typical Ures / U1mA | 1.77 | 1.77 | 1.77 | 1.75 | 1.75 | 1.73 | 1.73 | 1.72 | 1.71 | 1.7 | 1.7 | 1.64 | 1.63 | 1.59 | 1.58 | 1.54 |
repetitive charge transfer Qrs (C) | 0.5 | 0.5 | 0.5 | 0.6 | 0.6 | 0.6 | 0.6 | 1.6 | 1.6 | 1.8 | 1.8 | 2.4 | 2.4 | 3.2 | 4 | 6 |
guaranted 2ms test current (A) | 400 | 400 | 400 | 500 | 500 | 400 | 400 | 600 | 800 | 800 | 800 | 1000 | 1200 | 1500 | 2000 | 2500 |
max 2ms test current (A) | 400 | 400 | 400 | 600 | 600 | 500 | 500 | 800 | 900 | 900 | 900 | 1200 | 1400 | 1600 | 2100 | 3000 |
4/10µs high current test (kA) | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
nominal discharge current In (kA) | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 20 | 20 | 20 |
accelerated ageing test | 115℃ 0.9*U1mA/√2 Kct ≤ 1.0 |